Synthesis and characterization of multicomponent (CrNbTaTiW)C films for increased hardness and corrosion resistance
Multicomponent carbide thin films of (CrNbTaTiW)C (30–40 at.% C) with different metal contents were deposited at different temperatures using non-reactive DC magnetron sputtering. The lattice distortion for the metal lattice was estimated to vary from about 3 to 5%. Most films crystallized in the cu...