Synthesis and characterization of multicomponent (CrNbTaTiW)C films for increased hardness and corrosion resistance
Multicomponent carbide thin films of (CrNbTaTiW)C (30–40 at.% C) with different metal contents were deposited at different temperatures using non-reactive DC magnetron sputtering. The lattice distortion for the metal lattice was estimated to vary from about 3 to 5%. Most films crystallized in the cu...
Main Authors: | Paulius Malinovskis, Stefan Fritze, Lars Riekehr, Linus von Fieandt, Johan Cedervall, David Rehnlund, Leif Nyholm, Erik Lewin, Ulf Jansson |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2018-07-01
|
Series: | Materials & Design |
Online Access: | http://www.sciencedirect.com/science/article/pii/S0264127518302594 |
Similar Items
-
Influence of Deposition Temperature on the Phase Evolution of HfNbTiVZr High-Entropy Thin Films
by: Stefan Fritze, et al.
Published: (2019-02-01) -
Enhancing corrosion resistance, hardness, and crack resistance in magnetron sputtered high entropy CoCrFeMnNi coatings by adding carbon
by: León Zendejas Medina, et al.
Published: (2021-07-01) -
Influence of carbon on microstructure and mechanical properties of magnetron sputtered TaW coatings
by: S. Fritze, et al.
Published: (2020-11-01) -
Corrosion studies on multicomponent TiZrNbTa thin films
by: Jarlöv, Asker
Published: (2020) -
Synthesis and Characterisation of Nanocomposite Mo-Fe-B Thin Films Deposited by Magnetron Sputtering
by: Paulius Malinovskis, et al.
Published: (2021-04-01)