Crack-Growth Behavior in Thermal Barrier Coatings with Cyclic Thermal Exposure
Crack-growth behavior in yttria-stabilized zirconia-based thermal barrier coatings (TBCs) is investigated through a cyclic thermal fatigue (CTF) test to understand TBCs’ failure mechanisms. Initial cracks were introduced on the coatings’ top surface and cross section using the mi...
Main Authors: | Dowon Song, Taeseup Song, Ungyu Paik, Guanlin Lyu, Yeon-Gil Jung, Baig-Gyu Choi, In-Soo Kim, Jing Zhang |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2019-06-01
|
Series: | Coatings |
Subjects: | |
Online Access: | https://www.mdpi.com/2079-6412/9/6/365 |
Similar Items
-
Crack-Resistance Behavior of an Encapsulated, Healing Agent Embedded Buffer Layer on Self-Healing Thermal Barrier Coatings
by: Dowon Song, et al.
Published: (2019-05-01) -
Thermal Fatigue Behavior of Air-Plasma Sprayed Thermal Barrier Coating with Bond Coat Species in Cyclic Thermal Exposure
by: Ungyu Paik, et al.
Published: (2013-08-01) -
Comparative Study on Crack Initiation and Propagation of Glass under Thermal Loading
by: Yu Wang, et al.
Published: (2016-09-01) -
Stress Intensity Solutions of Thermally Induced Cracks in a Combustor Liner Hot Spot Using Finite Element Analysis
by: Rhymer, Donald William
Published: (2006) -
Thermal fatigue cracking of die-casting dies
by: Thermal fatigue cracking of die-casting dies, et al.
Published: (2010-01-01)