Reaction-Sintering Process for Ba5Nb4O15 and Sr5Nb4O15 Microwave Dielectric Ceramics and the Effect of Mg Addition
碩士 === 崑山科技大學 === 電子工程研究所 === 94 === Ba5Nb4O15 (BN) and Sr5Nb4O15 (SN) microwave dielectric ceramics prepared by a reaction-sintering process were investigated. The effect of Mg doping and CuO addition was also studied. In this process, the mixture of raw materials was pressed and sintered directly...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Published: |
2006
|
Online Access: | http://ndltd.ncl.edu.tw/handle/51194654810974985692 |
id |
ndltd-TW-094KSUT5428006 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-094KSUT54280062015-10-13T16:35:45Z http://ndltd.ncl.edu.tw/handle/51194654810974985692 Reaction-Sintering Process for Ba5Nb4O15 and Sr5Nb4O15 Microwave Dielectric Ceramics and the Effect of Mg Addition 反應燒結法製備Ba5Nb4O15與Sr5Nb4O15微波介電陶瓷及摻雜Mg之研究 ShihChung-yu 施宗佑 碩士 崑山科技大學 電子工程研究所 94 Ba5Nb4O15 (BN) and Sr5Nb4O15 (SN) microwave dielectric ceramics prepared by a reaction-sintering process were investigated. The effect of Mg doping and CuO addition was also studied. In this process, the mixture of raw materials was pressed and sintered directly without any calcination involved. Single phase BN and SN could be obtained. The sintering temperature was 50~100℃ lowered by Mg doping and 100~200℃ further lowered with CuO addition. With CuO addition, 97.3% and 96% of theoretic density were found in BN for 1450℃/4h sintering and SN fore 1430℃/4h sintering, respectively. Properties εr = 36.69~45.18, Q×f = 16,086~43,878 GHz, τf = 37.6~63.2 ppm/℃ for BN based and εr = 38.08~41.69, Q×f = 8,476~13,426 GHz, τf = 25.6~50.9 ppm/℃ for SN based ceramics were obtained. Yi-cheng Liou 劉依政 2006 學位論文 ; thesis 234 |
collection |
NDLTD |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 崑山科技大學 === 電子工程研究所 === 94 === Ba5Nb4O15 (BN) and Sr5Nb4O15 (SN) microwave dielectric ceramics prepared by a reaction-sintering process were investigated. The effect of Mg doping and CuO addition was also studied. In this process, the mixture of raw materials was pressed and sintered directly without any calcination involved. Single phase BN and SN could be obtained. The sintering temperature was 50~100℃ lowered by Mg doping and 100~200℃ further lowered with CuO addition. With CuO addition, 97.3% and 96% of theoretic density were found in BN for 1450℃/4h sintering and SN fore 1430℃/4h sintering, respectively. Properties εr = 36.69~45.18, Q×f = 16,086~43,878 GHz, τf = 37.6~63.2 ppm/℃ for BN based and εr = 38.08~41.69, Q×f = 8,476~13,426 GHz, τf = 25.6~50.9 ppm/℃ for SN based ceramics were obtained.
|
author2 |
Yi-cheng Liou |
author_facet |
Yi-cheng Liou ShihChung-yu 施宗佑 |
author |
ShihChung-yu 施宗佑 |
spellingShingle |
ShihChung-yu 施宗佑 Reaction-Sintering Process for Ba5Nb4O15 and Sr5Nb4O15 Microwave Dielectric Ceramics and the Effect of Mg Addition |
author_sort |
ShihChung-yu |
title |
Reaction-Sintering Process for Ba5Nb4O15 and Sr5Nb4O15 Microwave Dielectric Ceramics and the Effect of Mg Addition |
title_short |
Reaction-Sintering Process for Ba5Nb4O15 and Sr5Nb4O15 Microwave Dielectric Ceramics and the Effect of Mg Addition |
title_full |
Reaction-Sintering Process for Ba5Nb4O15 and Sr5Nb4O15 Microwave Dielectric Ceramics and the Effect of Mg Addition |
title_fullStr |
Reaction-Sintering Process for Ba5Nb4O15 and Sr5Nb4O15 Microwave Dielectric Ceramics and the Effect of Mg Addition |
title_full_unstemmed |
Reaction-Sintering Process for Ba5Nb4O15 and Sr5Nb4O15 Microwave Dielectric Ceramics and the Effect of Mg Addition |
title_sort |
reaction-sintering process for ba5nb4o15 and sr5nb4o15 microwave dielectric ceramics and the effect of mg addition |
publishDate |
2006 |
url |
http://ndltd.ncl.edu.tw/handle/51194654810974985692 |
work_keys_str_mv |
AT shihchungyu reactionsinteringprocessforba5nb4o15andsr5nb4o15microwavedielectricceramicsandtheeffectofmgaddition AT shīzōngyòu reactionsinteringprocessforba5nb4o15andsr5nb4o15microwavedielectricceramicsandtheeffectofmgaddition AT shihchungyu fǎnyīngshāojiéfǎzhìbèiba5nb4o15yǔsr5nb4o15wēibōjièdiàntáocíjícànzámgzhīyánjiū AT shīzōngyòu fǎnyīngshāojiéfǎzhìbèiba5nb4o15yǔsr5nb4o15wēibōjièdiàntáocíjícànzámgzhīyánjiū |
_version_ |
1717772685427081216 |