FATIGUE BEHAVIOR OF WELDED STRUCTURES

Fatigue is a phenomenon consisting of the accumulation of stresses and deformations that cause cracking and sometimes dismantling or even destruction of structures as a consequence of applying variable loads over time as intensity and position ( load cycles). The applied loads have values below t...

Full description

Bibliographic Details
Published in:	Fiabilitate şi Durabilitate
Main Authors:	Claudiu BABIS, Oana CHIVU, Andrei DIMITRESCU, Gabriel IACOBESCU, Anamaria FEIER, Augustin SEMENESCU
Format:	Article
Language:	English
Published:	Academica Brancusi 2018-05-01
Subjects:	fatigue cracking fracture
Online Access:	http://www.utgjiu.ro/rev_mec/mecanica/pdf/2018-01/07_Claudiu%20BABIS,%20%20Oana%20CHIVU,%20%20Andrei%20DIMITRESCU,%20Gabriel%20IACOBESCU,%20Anamaria%20FEIER,%20Augustin%20SEMENESCU%20-%20FATIGUE%20BEHAVIOR%20OF%20WELDED%20STRUCTURES.pdf

Similar Items

REHABILITATION TECHNIQUES APPLIED TO FILLET WELDED JOINTS IN ORDER TO INCREASE THE FATIGUE LIFE TIME
by: Claudiu BABIS, et al.
Published: (2018-05-01)

MAINTAINING IN OPERATION OF WELDED METAL STRUCTURES BY CHANGING THEIR USE
by: Anamaria FEIER, et al.
Published: (2018-05-01)

RISKES IN RADIOLOGY
by: Oana CHIVU, et al.
Published: (2018-05-01)

HISTORICAL WELDED STEEL STRUCTURES - QUALITY IN WELDING AND EXECUTION CLASSES ACCORDING TO SR EN-1090
by: Anamaria FEIER, et al.
Published: (2018-05-01)

Effect of welding defects on fatigue behavior of Ni-base superalloy GH4065A
by: LI Linhan, et al.
Published: (2024-08-01)

NOISE POLLUTION AT TURNING
by: Oana CHIVU, et al.
Published: (2018-05-01)

FATIGUE TEST AND CRACK PROPAGATION SIMULATION OF THE SMALL WELDED PIPE
by: CHEN MingYa, et al.
Published: (2021-01-01)

Fracture and fatigue behavior of Bambusa Vulgaris-Schrad Bamboo
by: Emmanuel O. Onche, et al.
Published: (2021-01-01)

THE INVESTIGATION OF A BUTT WELD WITH ULTRASOUND
by: Claudiu BABIS, et al.
Published: (2018-12-01)

Special Issue on Fracture and Fatigue Assessments of Structural Components
by: Alberto Campagnolo
Published: (2020-09-01)

Fatigue Strength and Fatigue Fracture Mechanism for Spot Welds in U-Shape Specimens
by: Mahmoud Shariati, et al.

THE INFLUENCE OF WELD SEAM SHAPE AND THE FATIGUE IN CASE OF THE FILLET WELDS
by: Claudiu BABIS, et al.
Published: (2015-12-01)

Fatigue Test and Unified Fatigue Life Calculation of Q460C Steel Notched Plates
by: Fengjun Lv, et al.
Published: (2023-03-01)

Dwell Fatigue Crack Growth Behavior of CP-Ti TA2 Welded Joint at 25 °C and 200 °C
by: Le Chang, et al.
Published: (2023-03-01)

RESEARCH ON THE FATIGUE CRACK PROPAGATION OF AIRCRAFT FUSELAGE SKIN UNDER UNIFORM PRESSURIZED LOAD (MT)
by: LIU LiPing, et al.
Published: (2023-01-01)

Experimental examination of fatigue life of welded joint with stress concentration
by: Miodrag Arsic, et al.
Published: (2016-03-01)

Experimental examination of fatigue life of welded joint with stress concentration
by: Miodrag Arsic, et al.
Published: (2016-03-01)

THE DETERMINATION AND APPRECIATION OF OCCUPATIONAL TOXICITY AT WORK
by: Oana CHIVU, et al.
Published: (2017-05-01)

FACTOR ANALYSIS OF QUALITY CHARACTERISTICS
by: Andrei DIMITRESCU, et al.
Published: (2017-05-01)

Numerical modeling and experimental estimates of structural member fatigue characteristics
by: Yu. P. Man’shin, et al.
Published: (2020-03-01)

Effect of Periodic Overloads on Short Fatigue Crack Behavior in CuNi<sub>2</sub>Si Alloy under Rotating Bending Load
by: Yahang Qin, et al.
Published: (2020-09-01)

Bending fatigue crack propagation behavior of U75V heavy rail steel
by: CEN Yaodong, et al.
Published: (2023-01-01)

SIMULATION OF EFFECTS OF GRAIN DISTRIBUTION MORPHOLOGY ON FATIGUE BEHAVIOR OF SHORT CRACKS AT WELD TOE (MT)
by: HU Ke, et al.
Published: (2023-01-01)

Influence of crack on welded joint characteristics in different types of loads
by: Burzić Zijah, et al.
Published: (2018-01-01)

Fatigue crack growth behavior and mechanism of aluminum alloy welded joints under overloads
by: XU Lianyong, et al.
Published: (2025-09-01)

Isothermal and thermomechanical fatigue interaction in fatigue crack propagation behavior of a low-carbon nitrogen-controlled 316 stainless steel
by: Yasuhiro Yamazaki
Published: (2019-02-01)

Isothermal and thermomechanical fatigue interaction in fatigue crack propagation behavior of a low-carbon nitrogen-controlled 316 stainless steel
by: Yasuhiro Yamazaki
Published: (2019-04-01)

ANALYSIS OF FATIGUE FRACTURE BASED ON PERIDYNAMIC
by: 石宏顺, et al.
Published: (2018-01-01)

Fatigue Crack Growth Behavior of Austempered AISI 4140 Steel with Dissolved Hydrogen
by: Varun Ramasagara Nagarajan, et al.
Published: (2017-11-01)

Effect of laser welding heat input on fatigue crack growth and CTOD fracture toughness of HSLA steel joints
by: Henrique Varella Ribeiro, et al.
Published: (2021-03-01)

Fatigue crack behavior on a Cu-Zn-Al SMA
by: V. Di Cocco, et al.
Published: (2014-09-01)

Research Status of Initiation and Expansion Behavior of Gear Fatigue Cracks
by: Yuan Jie, et al.
Published: (2023-05-01)

Biaxial Very High Cycle Fatigue Testing and Failure Mechanism of Welded Joints in Structural Steel Q345
by: Bing Xue, et al.
Published: (2024-09-01)

Experimental and analytical investigation on cryogenic fatigue and fracture behavior of 5% Ni steel welded joints for LEG type B cargo tank
by: Qing-Hua Zhou, et al.
Published: (2025-10-01)

Fatigue crack growth analysis of welded bridge details
by: Danilo D�Angela, et al.
Published: (2022-04-01)

Fatigue crack growth in welded S355 specimens subjected to combined loading
by: J. Lewandowski, et al.
Published: (2019-04-01)

FEM Analysis of the Welding Seams Geometry in Case of Fillet Welds
by: Babiş Claudiu, et al.
Published: (2021-01-01)

Fatigue Behavior of Al 7075-T6 Plates Repaired with Composite Patch under the Effect of Overload
by: Bel Abbes Bachir Bouiadjra, et al.
Published: (2021-12-01)

Propagation of Fatigue Cracks in Friction of Brittle Hydrogels
by: Tetsuo Yamaguchi, et al.
Published: (2018-06-01)

Development of in-situ fatigue crack observing system for rotating bending fatigue testing machine
by: B. Lian, et al.
Published: (2015-12-01)