| 總結: | Copper smelting slag usually contains 1–6 wt% copper, which can be recovered by pyrometallurgical and flotation processes. However, the tailing slags still consist of 0.3–0.7 wt% Cu and 35–45 wt% Fe equivalents to those in the copper and iron ores, respectively. Most of the research was focused on the recovery of iron from the tailing slags. Copper can increase the mechanical strength, corrosion resistance and antibacterial property of some steels. A new process to recover copper and iron directly and fully from hot copper smelting slag is proposed to produce Cu-Fe alloy for steel production. Effects of flux, temperature, reaction time, reductant type and addition on the recovery of copper and iron were investigated by high-temperature experiments and thermodynamic calculations. It was found that, with 5% CaO and 13–16% carbon additions, most of the copper and iron can be recovered from copper smelting slag at 1350–1400 °C. The copper and iron contents of the reduced slag are lower than 0.1% and 0.5%, respectively, at optimum condition. The new process has the advantages of low energy consumption, low flux addition and high recovery of copper and iron.
|
|---|