Very high cycle fatigue strength and crack growth of thin steel sheets

Show other versions (1)

For basic observations or for industrial applications it is of interest to use flat specimens at very high frequency in the gigacycle regime. In this work, thin flat sheet, with 1.2 mm thickness of a complex phase ferrite-martensitic steels were considered for carrying out fatigue tests at high freq...

Full description

Bibliographic Details
Published in:	Fracture and Structural Integrity
Main Authors:	Mohand Ouarabi, Ruben Perez Mora, Claude Bathias, Thierry Palin-Luc
Format:	Article
Language:	English
Published:	Gruppo Italiano Frattura 2016-03-01
Subjects:	Ultrasonic fatigue Plate steel fatigue Fatigue resistance Fatigue crack growth
Online Access:	http://www.gruppofrattura.it/pdf/rivista/numero36/numero_36_art_11.pdf

Similar Items

Very high cycle fatigue strength and crack growth of thin steel sheets
by: Mohand Ouarabi, et al.
Published: (2016-03-01)

Crack path in aeronautical titanium alloy under ultrasonic torsion loading
by: A. Nikitin, et al.
Published: (2015-12-01)

Research Status of Initiation and Expansion Behavior of Gear Fatigue Cracks
by: Yuan Jie, et al.
Published: (2023-05-01)

Crack path in aeronautical titanium alloy under ultrasonic torsion loading
by: A. Nikitin, et al.
Published: (2016-01-01)

Development of a small-punch-fatigue test method to evaluate fatigue strength and fatigue crack propagation
by: Yamazaki Yasuhiro, et al.
Published: (2024-06-01)

In-Situ Thermography Investigation of Crack Growth in Armco Iron under Gigacycle Fatigue Loading
by: Victor Postel, et al.
Published: (2022-05-01)

Development of in-situ fatigue crack observing system for rotating bending fatigue testing machine
by: B. Lian, et al.
Published: (2015-12-01)

Isothermal and thermomechanical fatigue interaction in fatigue crack propagation behavior of a low-carbon nitrogen-controlled 316 stainless steel
by: Yasuhiro Yamazaki
Published: (2019-02-01)

Isothermal and thermomechanical fatigue interaction in fatigue crack propagation behavior of a low-carbon nitrogen-controlled 316 stainless steel
by: Yasuhiro Yamazaki
Published: (2019-04-01)

CHARACTERIZATION OF NOTCH FATIGUE CRACK INITIATION AND PROPAGATION OF INDUSTRIAL PURE TITANIUM BASED ON DIC
by: BAO QiLe, et al.
Published: (2024-10-01)

Fatigue Crack Growth in a Monocrystal and Its Similarity to Short-Crack Propagation in a Polycrystal of Nickel
by: Avihai Petel, et al.
Published: (2023-04-01)

Very High Cycle Fatigue of Welds: A Review
by: Andrew England, et al.
Published: (2023-11-01)

A four-parameters model for fatigue crack growth data analysis
by: G.P. Pucillo, et al.
Published: (2013-10-01)

Study of short cracks under biaxial fatigue
by: P. Lopez-Crespo, et al.
Published: (2014-10-01)

Fatigue crack propagation in short-fiber reinforced plastics
by: K. Tanaka, et al.
Published: (2015-09-01)

Prediction and Analysis of Bending Fatigue Crack Growth Behavior of Spur Gear
by: Liu Xinbo, et al.
Published: (2016-01-01)

Initiation and growth behavior of very-long microstructurally short fatigue cracks
by: P. Lorenzino, et al.
Published: (2013-07-01)

Fatigue crack behavior on a Cu-Zn-Al SMA
by: V. Di Cocco, et al.
Published: (2014-09-01)

High-Cycle Fatigue Life and Strength Prediction for Medium-Carbon Bainitic Steels
by: Yusong Fan, et al.
Published: (2022-05-01)

RESEARCH ON FATIGUE CRACK PROPAGATION CHARACTERISTICS AND REMAINING LIFE AT THE TOOTH ROOT OF A GEAR
by: GAO Yun, et al.
Published: (2019-01-01)

THE STUDY OF THE STAGES OF NUCLEATION AND GROWTH OF CRACKS DURING THE FULL-SCALE FATIGUE TEST
by: I. O. Vakulenko, et al.
Published: (2008-03-01)

On a kinked crack model to describe the influence of material microstructure on fatigue crack growth
by: Andrea Spagnoli, et al.
Published: (2013-07-01)

Cracking directions in multiaxial low cycle fatigue at high and room temperatures
by: Masao Sakane, et al.
Published: (2017-07-01)

Cracking directions in multiaxial low cycle fatigue at high and room temperatures
by: Masao Sakane, et al.
Published: (2017-06-01)

Cracking directions in multiaxial low cycle fatigue at high and room temperatures
by: Masao Sakane, et al.
Published: (2017-06-01)

Experimental and Numerical Study on Crack Propagation of Cracked Plates under Low Cycle Fatigue Loads
by: Dong Qin, et al.
Published: (2023-07-01)

Very High Cycle Fatigue (VHCF) of notched specimens: a review
by: Paolo Zuliani, et al.
Published: (2025-09-01)

Ultrasonic fatigue testing of AISI 304 and 316 stainless steels under environmental and immersion conditions
by: Luis M. Torres Duarte, et al.
Published: (2024-04-01)

In-Depth Understanding of Fatigue Micromechanisms in Cemented Carbides: Implications for Optimal Microstructural Tailoring
by: Luis Llanes
Published: (2019-08-01)

Accelerated estimation of the very high cycle fatigue strength and life of polymer composites under ultrasonic cyclic three-point bending
by: Aravind Premanand, et al.
Published: (2024-04-01)

RESEARCH ON THE FATIGUE CRACK PROPAGATION OF AIRCRAFT FUSELAGE SKIN UNDER UNIFORM PRESSURIZED LOAD (MT)
by: LIU LiPing, et al.
Published: (2023-01-01)

Biaxial Very High Cycle Fatigue Testing and Failure Mechanism of Welded Joints in Structural Steel Q345
by: Bing Xue, et al.
Published: (2024-09-01)

On fatigue behavior of two spring steels. Part I: Wöhler curves and fractured surfaces
by: D. Angelova, et al.
Published: (2016-06-01)

On fatigue behavior of two spring steels. Part I: Wöhler curves and fractured surfaces
by: D.Angelova, et al.
Published: (2016-07-01)

On the Link between Plastic Wake Induced Crack Closure and the Fatigue Threshold
by: Rhys Jones, et al.
Published: (2024-04-01)

Fatigue crack growth analysis on square prismatic with embedded cracks under tension loading
by: M.S. Shaari, et al.
Published: (2017-03-01)

Analysis of initial crack path in fretting fatigue
by: J. Vázquez, et al.
Published: (2016-07-01)

Analysis of initial crack path in fretting fatigue
by: J. Vazquez, et al.
Published: (2016-06-01)

The effect of steady torsion on fatigue crack growth under rotating bending loading on aluminium alloy 7075-T6
by: M. da Fonte, et al.
Published: (2014-10-01)

Development of in-situ fatigue crack observing system for rotating bending fatigue testing machine
by: B. Lian, et al.
Published: (2016-02-01)