Correlation of Sampling Orientation and Impact Toughness of HTP Line-Pipe Steel Strip

Test results indicated that 14.3 mm HTP line-pipe steel strip(0.056C,1.21Mn,0.07Nb,0.01Ti)had  seriols anisotropy, the charpy V-otshimpact energy and delamiratig crack tendency of sample perallelod to rling lirec- ton wls obviously higher han that of samples being45° and vetical o mling diecion at s...

وصف كامل

التفاصيل البيبلوغرافية
الحاوية / القاعدة:Teshugang
المؤلفون الرئيسيون: Zhu Lixia, Wang Yalong, Li Jinfeng, Chen Hongda, He Xiaodong
التنسيق: مقال
اللغة:الصينية
منشور في: Editorial Office of Special Steel 2008-01-01
الموضوعات:
HTP Line-pipe Steel
Impact Toughness
Delaminating Crack
Sampling Orientation
الوصول للمادة أونلاين:http://www.specialsteeljournal.com/thesisDetails?columnId=129772084&Fpath=home&index=0
الوصف
الملخص:Test results indicated that 14.3 mm HTP line-pipe steel strip(0.056C,1.21Mn,0.07Nb,0.01Ti)had  seriols anisotropy, the charpy V-otshimpact energy and delamiratig crack tendency of sample perallelod to rling lirec- ton wls obviously higher han that of samples being45° and vetical o mling diecion at same icmperature. The ddlami- naig eack was calaed by stip deice, it we efeied dialoeation confguation wih cerain direstion feature and related to temperature.