| Summary: | Previous experiments pointed out that the deviation using a sphere as reference of graphite particles is noticeably increased by Si-alloying, with inoculation as a possible beneficial effect. The main objective of the present work is to evaluate the effects of commercial inoculants (Ca/Ca, Ba/Ca, RE-FeSi alloys) on 4.5%Si ductile iron, thin wall castings. FeSiMgRE treated iron (0.032–0.036%Mg<sub>res</sub>) is in-mold inoculated (a four-work-positions pattern). A complex chemical composition is obtained for each inoculation variant. Wedge casting W<sub>3</sub> (ASTM A 367) is used to evaluate structure characteristics at different wall thickness (3–15 mm). Minimum and maximum size, area, nodule count, and representative graphite shape factors are evaluated. Roundness (including A<sub>G</sub> and F<sub>max</sub>) at 0.6–0.8 level illustrates the common formation of slightly irregular spheroidal graphite (Type V, ISO 945). Ca, RE-FeSi inoculation leads to the highest level of real perimeter and, consequently, to the lowest level of Sphericity. Ca, Ba-FeSi inoculation appears to be better than simple Ca-FeSi for improving graphite parameters, while Ca, RE-FeSi has the lowest beneficial effect, especially as it negatively affects the compactness degree of graphite particles. A two-step liquid treatment using RE-bearing FeSiCaMg master alloy and Ca, Ba-FeSi inoculant appears to be a solution to improve graphite parameters for high-Si ductile irons solidified in thin wall castings.
|
|---|