CORROSION DEGRADATION OF S235JR AND S355JR STEELS USED IN THE CONSTRUCTION OF SURFACE MINING EQUIPMENT
Metal structures exposed to aggressive environmental conditions are often subject to the loss of protective layers and material degradation over time due to corrosion. This leads to a reduction in the cross-sectional area of the components, an increase in surface roughness, the formation of surfa...
| Published in: | Fiabilitate şi Durabilitate |
|---|---|
| Main Author: | |
| Format: | Article |
| Language: | English |
| Published: |
Academica Brancusi
2024-12-01
|
| Subjects: | |
| Online Access: | https://www.utgjiu.ro/rev_mec/mecanica/pdf/2024-02/04_Ciofu%20F-CORROSION%20DEGRADATION%20OF%20S235JR%20AND%20S355JR%20STEELS%20USED%20IN%20THE%20CONSTRUCTION%20OF%20SURFACE%20MINING%20EQUIPMENT.pdf |
| _version_ | 1849495503818981376 |
|---|---|
| author | Florin CIOFU |
| author_facet | Florin CIOFU |
| author_sort | Florin CIOFU |
| collection | DOAJ |
| container_title | Fiabilitate şi Durabilitate |
| description | Metal structures exposed to aggressive environmental conditions are often subject to
the loss of protective layers and material degradation over time due to corrosion. This leads to a
reduction in the cross-sectional area of the components, an increase in surface roughness, the
formation of surface irregularities and corrosion cavities, as well as a decline in the overall set of
physical and mechanical properties. The aim of this study is to analyze the fatigue behavior of
low-alloy steels under corrosive conditions, specifically those used in the construction of mining
equipment for various mining operations in Gorj County |
| format | Article |
| id | doaj-art-e3d9a0cede784f08824ca2b656c7d6cb |
| institution | Directory of Open Access Journals |
| issn | 1844-640X 2344-3669 |
| language | English |
| publishDate | 2024-12-01 |
| publisher | Academica Brancusi |
| record_format | Article |
| spelling | doaj-art-e3d9a0cede784f08824ca2b656c7d6cb2025-08-20T03:06:04ZengAcademica BrancusiFiabilitate şi Durabilitate1844-640X2344-36692024-12-011722331CORROSION DEGRADATION OF S235JR AND S355JR STEELS USED IN THE CONSTRUCTION OF SURFACE MINING EQUIPMENTFlorin CIOFU0Engineering Faculty, ”Lucian Blaga” University of Sibiu, ROMANIAMetal structures exposed to aggressive environmental conditions are often subject to the loss of protective layers and material degradation over time due to corrosion. This leads to a reduction in the cross-sectional area of the components, an increase in surface roughness, the formation of surface irregularities and corrosion cavities, as well as a decline in the overall set of physical and mechanical properties. The aim of this study is to analyze the fatigue behavior of low-alloy steels under corrosive conditions, specifically those used in the construction of mining equipment for various mining operations in Gorj Countyhttps://www.utgjiu.ro/rev_mec/mecanica/pdf/2024-02/04_Ciofu%20F-CORROSION%20DEGRADATION%20OF%20S235JR%20AND%20S355JR%20STEELS%20USED%20IN%20THE%20CONSTRUCTION%20OF%20SURFACE%20MINING%20EQUIPMENT.pdfcorrosionso2 (ppm)temperaturehumidityuv radiation |
| spellingShingle | Florin CIOFU CORROSION DEGRADATION OF S235JR AND S355JR STEELS USED IN THE CONSTRUCTION OF SURFACE MINING EQUIPMENT corrosion so2 (ppm) temperature humidity uv radiation |
| title | CORROSION DEGRADATION OF S235JR AND S355JR STEELS USED IN THE CONSTRUCTION OF SURFACE MINING EQUIPMENT |
| title_full | CORROSION DEGRADATION OF S235JR AND S355JR STEELS USED IN THE CONSTRUCTION OF SURFACE MINING EQUIPMENT |
| title_fullStr | CORROSION DEGRADATION OF S235JR AND S355JR STEELS USED IN THE CONSTRUCTION OF SURFACE MINING EQUIPMENT |
| title_full_unstemmed | CORROSION DEGRADATION OF S235JR AND S355JR STEELS USED IN THE CONSTRUCTION OF SURFACE MINING EQUIPMENT |
| title_short | CORROSION DEGRADATION OF S235JR AND S355JR STEELS USED IN THE CONSTRUCTION OF SURFACE MINING EQUIPMENT |
| title_sort | corrosion degradation of s235jr and s355jr steels used in the construction of surface mining equipment |
| topic | corrosion so2 (ppm) temperature humidity uv radiation |
| url | https://www.utgjiu.ro/rev_mec/mecanica/pdf/2024-02/04_Ciofu%20F-CORROSION%20DEGRADATION%20OF%20S235JR%20AND%20S355JR%20STEELS%20USED%20IN%20THE%20CONSTRUCTION%20OF%20SURFACE%20MINING%20EQUIPMENT.pdf |
| work_keys_str_mv | AT florinciofu corrosiondegradationofs235jrands355jrsteelsusedintheconstructionofsurfaceminingequipment |