CORROSION DEGRADATION OF S235JR AND S355JR STEELS USED IN THE CONSTRUCTION OF SURFACE MINING EQUIPMENT

Metal structures exposed to aggressive environmental conditions are often subject to the loss of protective layers and material degradation over time due to corrosion. This leads to a reduction in the cross-sectional area of the components, an increase in surface roughness, the formation of surfa...

Full description

Bibliographic Details
Published in:	Fiabilitate şi Durabilitate
Main Author:	Florin CIOFU
Format:	Article
Language:	English
Published:	Academica Brancusi 2024-12-01
Subjects:	corrosion so2 (ppm) temperature humidity uv radiation
Online Access:	https://www.utgjiu.ro/rev_mec/mecanica/pdf/2024-02/04_Ciofu%20F-CORROSION%20DEGRADATION%20OF%20S235JR%20AND%20S355JR%20STEELS%20USED%20IN%20THE%20CONSTRUCTION%20OF%20SURFACE%20MINING%20EQUIPMENT.pdf

Similar Items

Experimental analysis of atmospheric corrosion of steel S235JR in industrial environment
by: Stefanović Jelena N., et al.
Published: (2025-01-01)

The Influence of Different Type Materials of Grit Blasting on the Corrosion Resistance of S235JR Carbon Steel
by: Nicoleta Bogatu, et al.
Published: (2023-02-01)

RESEARCH ON DEGRADATION CORROSIVE ENVIRONMENT OF SOME STEELS USED IN MANUFACTURING MINING EQUIPMENT. MECHANICAL TESTS
by: Florin CIOFU, et al.
Published: (2017-05-01)

Corrosion Behavior of S235JR Carbon Steel in 0.5 M HCl Solution During 24 Weeks
by: Alina Crina Mureșan, et al.
Published: (2025-09-01)

Microvoids Evolution in S235JR Steel Subjected to Multi-Axial Stress State
by: Paweł Grzegorz KOSSAKOWSKI, et al.
Published: (2014-08-01)

Finite element type of stress analysis for parts based on S235 JR steel welding
by: C. Babis, et al.
Published: (2014-04-01)

Bead-On-Plate Welding on S235JR Steel by Underwater Local Dry Chamber Process
by: Rogalski Grzegorz, et al.
Published: (2014-04-01)

Mechanical Strengthening in S235JR Steel Sheets through Vibration-Assisted Ball Burnishing
by: Jordi Llumà, et al.
Published: (2020-07-01)

Effect of Fiber-Laser Parameters on Cutting Accuracy of Thin and Thick S355JR Structural Steel Plates
by: Laura Cepauskaite, et al.
Published: (2024-06-01)

The Effect of Nopal Mucilage Addition on the Corrosion Rate of Reinforcement Steel in Concrete
by: Enrique Martínez-Barrios, et al.
Published: (2025-04-01)

RESEARCH ON DEGRADATION CORROSIVE ENVIRONMENT OF SOME STEELS USED IN MANUFACTURING MINING EQUIPMENT. MICROSCOPIC ANALYSIS
by: Florin CIOFU, et al.
Published: (2017-05-01)

THE INFLUENCE OF SOME CORROSIVE ENVIRONMENTS ON THE WORKING EQUIPMENT OF THE HEAT EXCHANGERS
by: Florin CIOFU, et al.
Published: (2014-05-01)

UV radiation effect on the corrosion inhibition potential of Helichrysum kraussii plant extract on mild steel metal in sulphuric acid medium
by: T. Sithuba, et al.
Published: (2024-06-01)

Strength of the Bond of Structural Steel S235JR to Bronze SAE660 Produced by Casting in Pre-Mold
by: Zaheri M., et al.
Published: (2017-09-01)

Effect of Initial Porosity on Material Response Under Multi-Axial Stress State for S235JR Steel
by: Kossakowski P.G.
Published: (2012-12-01)

Experimental determination of the void volume fraction for S235JR steel at failure in the range of high stress triaxialities
by: Kossakowski P. G.
Published: (2017-03-01)

Influence of Air Pollution Factors on Corrosion of Metal Equipment in Transmission and Transformation Power Stations
by: Xiufang Chen, et al.
Published: (2022-06-01)

Corrosion Resistance of Steel S355MC in Crude Glycerol
by: Marián Palcut, et al.
Published: (2023-05-01)

Research of Corrosion Behavior of Q235 Steel in Wuhan Soil
by: XU Li, ZHOU Xue-jie, ZHENG Peng-hua, WU Jian-ping, WU Jun
Published: (2022-02-01)

STUDY OF S235 STEEL CORROSION PROCESS IN WASTEWATER FROM THE PETROCHEMICAL INDUSTRY
by: Julieta Daniela CHELARU, et al.
Published: (2019-06-01)

An analysis of structures occurring in weld deposit of steel S235JR+N with tungsten carbide particles and martensitic matrix
by: J. Kozak, et al.
Published: (2019-01-01)

Properties and Microstructure of Laser Welded Dissimilar Joints of TP347-HFG and S235JR Steels with Additional Material
by: H. Danielewski, et al.
Published: (2020-07-01)

Improvement in the Design of Welded Joints of EN 235JR Low Carbon Steel by Multiple Response Surface Methodology
by: Ruben Lostado Lorza, et al.
Published: (2016-08-01)

Utilization of diffraction analysis in the study of martensitic weld deposits using tungsten carbide particles on S235JR+N steel
by: J. Kozák, et al.
Published: (2020-01-01)

Analysis of the possibility of applying a residual magnetic field for lack of fusion detection in welded joints of S235JR steel
by: Złocki Arkadiusz, et al.
Published: (2025-06-01)

Experimental Research on the Influence of Structural Modifications of Adherends on the Load - Bearing Capacity of Lap Joints of S235JR Steel Sheets
by: Władysław Zielecki, et al.
Published: (2023-01-01)

Effect of the Stress State Triaxiality on the Value of Limit Strain of Micro-Void Development in S235JR Steel - Numerical Analysis
by: Wiktor Wcislik
Published: (2011-12-01)

Atmospheric corrosion of metals under conditions of air pollution
by: Vladimir Vujičić
Published: (1996-07-01)

A Study on the Corrosion Inhibition Performance of Various Starches for Q235A Steel
by: Di MA, et al.
Published: (2025-06-01)

Corrosion investigations of P235 carbon steel in deionized water
by: Ladislav Vrsalović, et al.
Published: (2019-09-01)

Corrosion resistance of micro-arc oxidation composite coatings on S355 offshore steel
by: HE Xing, et al.
Published: (2019-09-01)

Research on corrosion performance of Q235B steel in industrial coastal atmospheric environment
by: Wenjuan Chen, et al.
Published: (2024-10-01)

Comparative Study of Corrosion Rates Determined by Several Methods for Q235 Steel
by: CHEN Xin-xin, GUAN Lei, LI Wan-jiang, ZHANG Xiao-dong, FU Yi-ping, LI Yu
Published: (2021-02-01)

Effect of cyclic high temperature fluctuations on the corrosion failure of S40900, S43036, S31635 and S44400 stainless steels
by: Roland Tolulope Loto
Published: (2021-01-01)

Corrosion Behavior of Q235 Steel and Hot-Dip Galvanized Steel in Brown Soil Environment
by: YAO Xin, CHEN Hao, ZHOU Xuejie, WANG Jingyu, YU Jianfei, ZHANG Ming, WU Jun, CHEN Zhijian
Published: (2024-10-01)

Caio Prado Jr.
by: PEDRO CEZAR OUTRA FONSECA
Published: (2023-11-01)

BARBATO JR, Roberto.
by: Editor REA
Published: (2021-05-01)

Key parameters of soil corrosivity and a model for predicting the corrosion rate of Q235 steel in Beijing
by: Zhibiao YIN, et al.
Published: (2023-11-01)

JrATHB-12 mediates JrMYB113 and JrMYB27 to control the anthocyanin levels in different types of red walnut
by: Haifeng Xu, et al.
Published: (2024-08-01)

Influence of UV light on the corrosion behavior of AA6061-T6 in a CMA solution
by: Linyan Zhang, et al.
Published: (2023-05-01)