Effect of Low Water Content and Temperature on Corrosion Behavior of X80 Pipeline Steel in Shenyang Soil Simulated Solution

Aiming at exploring the effect of low water content and temperature on the electrochemical corrosion behavior of X80 pipeline steel in Shenyang soil simulated solution，the data of impedance spectrum and polarization curve were measured by weight loss test，AC impedance technique and potentiodynamic p...

Full description

Bibliographic Details
Published in:	Cailiao Baohu
Main Author:	ZHANG Xiaolong
Format:	Article
Language:	Chinese
Published:	Editorial Department of Materials Protection 2023-07-01
Subjects:	water content；temperature；corrosion；x80 pipeline steel；shenyang meadow soil
Online Access:	http://www.mat-pro.com/fileup/1001-1560/PDF/230708.pdf

Similar Items

Study on Stress Corrosion Behavior of X100 and X80 Pipeline Steels with Applied Potential
by: HUANG Tao, GUO Jie, WEI Kai-hua, CHEN Jia-qi, XUE Hui-yong, WANG Xiao-feng
Published: (2023-03-01)

Study on the Influence of Sodium Chloride Concentration on the Electrochemical Corrosion Behavior of X80 Pipeline Steel Base Material and Weld Zone
by: ZHANG Ying, YANG Yuzhi, YU Liusi, WANG Yijia
Published: (2024-04-01)

Effects of Welding Heat Input on Microstructure and Corrosion Characterization in CGHAZ of X80 Pipeline Steel
by: Xue-Mei Wang, et al.
Published: (2023-06-01)

Progress and prospects of research and application of X80 pipeline steel and steel pipe in China
by: Yaorong FENG, et al.
Published: (2020-06-01)

Corrosion behavior of the weld joint of X80 pipeline steel in an acidic red soil
by: Xianming Cao, et al.
Published: (2020-01-01)

Insight into sulfate-reducing bacteria corrosion behavior of X80 pipeline steel welded joint in a soil solution
by: Mengdi Yan, et al.
Published: (2023-05-01)

Effect of applied potentials on the corrosion of X80 pipeline steel in simulated coastal soil solution
by: Jing MA, et al.
Published: (2023-12-01)

Influence of riboflavin on the corrosion of X80 pipeline steel by Sulfate reducing bacteria
by: Lei Fu, et al.
Published: (2024-01-01)

Insight into the Role of Mo Content on the Microstructure and Impact Toughness of X80 Thick-Walled Low-Temperature Pipeline Steel
by: Jinxing Jiang, et al.
Published: (2023-08-01)

Simulation analysis of X80 pipeline steel welding
by: M. M. Li, et al.
Published: (2023-01-01)

Corrosion testing of X52 and X80 steels immersed in stimulated emulsions using a real petroleum sample
by: L.M. Quej-Ake, et al.
Published: (2024-06-01)

Effect of Rolling Process on Structure, Texture and Properties of X80 Pipeline Steel
by: Han Le, et al.
Published: (2012-10-01)

Effects of alternating current on microbiologically synergistic corrosion of pipeline steel X80 applied by elastic stress
by: Zheng Cai, et al.
Published: (2024-03-01)

Study on Biofilm Forming Microorganisms Associated with the Biocorrosion of X80 Pipeline Steel in Produced Water from Oilfield
by: Edkarlla S. D. de Oliveira, et al.
Published: (2021-10-01)

Influence of hydrogen environment on fatigue fracture morphology of X80 pipeline steel
by: Jingxuan Zhuo, et al.
Published: (2023-01-01)

Effect of Cr on Phase Transformation and Structure of 0.035C-0.12Nb X80 Pipeline Steel
by: Niu Yanlong, et al.
Published: (2009-11-01)

Stress corrosion of HAZ subdivision of X80 pipeline steel in sterile high-sulfate soil
by: Youjun Yu, et al.
Published: (2023-09-01)

Test for effect of welding layers on girth weld toughness of X80 pipeline steel
by: Ting WANG, et al.
Published: (2022-04-01)

Effect of Ce Content on Microstructure and Corrosion Resistance of X100 Pipeline Steel
by: LIU Peng, YANG Ji-chun, LI An-xin, LIU Xiang-jun, YANG Chang-qiao, GONG Lei
Published: (2023-05-01)

Study of Tensile Deformation and Damage Law in Undermatching X80 Pipeline Steel Welded Joints
by: Yongbin Que, et al.
Published: (2023-01-01)

Limit width analysis of X80 corroded pipeline pass through landslide
by: Peng ZHANG, et al.
Published: (2022-08-01)

Experimental Study on Dephosphorization of X80 Pipeline Steel by Duplex Steelmaking Technology for Combined Blowing Converter
by: Zhao Bin, et al.
Published: (2023-03-01)

Hydrogen Embrittlement Sensitivity of X80 Pipeline Steel Welded Joints in Hydrogen Environment
by: LI Tianlei, LI Ke, SHI Daiyan, FENG Min, YANG Zhiwen, CHEN Yingfeng, WANG Xiuyun, LIN Yuanhua, YU Zifeng
Published: (2024-04-01)

Progress of research on key influencing factors of stress corrosion cracking of X80 buried pipeline
by: Cheng SUN, et al.
Published: (2021-09-01)

Relationship between coercivity and stress of X80 pipeline steel
by: CHENG Fanju, et al.
Published: (2022-11-01)

Corrosion of X65 Pipeline Steel Under Deposit and Effect of Corrosion Inhibitor
by: XU Yun-ze, et al.
Published: (2016-10-01)

Effect of Heat Input on Microstructure and Corrosion Resistance of X80 Laser Welded Joints
by: Wei Zhao, et al.
Published: (2022-09-01)

The effect of X80 steel microstructure on CO inhibition of hydrogen embrittlement
by: Qin WANG, et al.
Published: (2022-03-01)

Effect of pre-strain on microstructure evolution and fracture behavior of undermatching X80 pipeline steel girth weld
by: Lianshuang Dai, et al.
Published: (2024-01-01)

Corrosion Behavior of X80 Pipe Steel under HVDC Interference in Sandy Soil
by: Runzhi Qin, et al.
Published: (2018-10-01)

Effect of Cooling Rate of Hot-Deformed Austenite on Structure and Property of X80 Pipeline Steel
by: Zeng Xianping, et al.
Published: (2010-10-01)

Reinforcement test of epoxy-filled steel sleeves for girth weld defects of X80 pipelines
by: Dongliang YU, et al.
Published: (2021-09-01)

Study on Corrosion Resistance and Hydrogen Permeation Behavior in Inter-Critically Reheated Coarse-Grained Heat-Affected Zone of X80 Pipeline Steel
by: Kai Chen, et al.
Published: (2022-07-01)

STUDY OF DYNAMIC FRACTURE OF X80 NATURAL GAS PIPELINE
by: LV JinJie, et al.
Published: (2018-01-01)

Stress corrosion cracking behavior of X80 steel under the combined effects of sulfide and cathodic potential
by: Xinyi Liu, et al.
Published: (2023-05-01)

Quantitative Study on Hydrogen Concentration–Hydrogen Embrittlement Sensitivity of X80 Pipeline Steel Based on Hydrogen Permeation Kinetics
by: Rundong Zhang, et al.
Published: (2024-06-01)

Stress corrosion cracking behavior of X80 pipeline steel under alternating current, Desulfovibrio desulfurican and cathodic protection potential
by: Qi Fu, et al.
Published: (2023-05-01)

Ductile Fracture Prediction of X80 Pipeline Steel Using Void Growth Model
by: Chunjian Feng, et al.
Published: (2022-05-01)

Mechanistic investigations of corrosion and localized corrosion of X80 steel in seawater comprising sulfate-reducing bacteria under continuous carbon starvation
by: Hongwei Liu, et al.
Published: (2022-12-01)

Russian architectural and cultural heritage in Shenyang
by: Михаил Базилевич
Published: (2025-04-01)