Physicochemical Properties of Silicon Cast Iron

• 發表在: Archives of Foundry Engineering
• Main Authors: Stawarz M., Kajzer W., Kajzer A., Dojka M.
• 格式: Article
• 語言: 英语
• 出版: Polish Academy of Sciences 2017-06-01
• 主題: Pitting corrosion; Alloy cast iron; SiMo; Silicon cast iron
• 在線閱讀: http://www.degruyter.com/view/j/afe.2017.17.issue-2/afe-2017-0059/afe-2017-0059.xml?format=INT

The article presents results of pitting corrosion studies of selected silicon cast irons. The range of studies included low, medium and high silicon cast iron. The amount of alloying addition (Si) in examined cast irons was between 5 to 25 %. Experimental melts of silicon cast irons [1-3] were conducted in Department of Foundry of Silesian University of Technology in Gliwice and pitting corrosion resistance tests were performed in Faculty of Biomedical Engineering in Department of Biomaterials and Medical Devices Engineering of Silesian University of Technology in Zabrze. In tests of corrosion resistance the potentiostat VoltaLab PGP201 was used. Results obtained in those research complement the knowledge about the corrosion resistance of iron alloys with carbon containing Si alloying addition above 17 % [4-6]. Obtained results were supplemented with metallographic examinations using scanning electron microscopy. The analysis of chemical composition for cast irons using Leco spectrometer was done and the content of alloying element (silicon) was also determined using the gravimetric method in the laboratory of the Institute of Welding in Gliwice. The compounds of microstructure were identify by X-ray diffraction.