Crack Initiation in Ni-Based Single Crystal Superalloy under Low-Cycle Fatigue-Oxidation Conditions

The mechanism of oxidation-assisted initiation of surface cracks of a fourth-generation Ni-based single crystal superalloy was systematically investigated during low cycle fatigue at 900 °C and 980 °C. The results show that cracks initiate near the surface defects at 900 °C, while they initiate in t...

Full description

Bibliographic Details

Published in:	Metals
Main Authors:	Pengfei Wang, Xinbao Zhao, Quanzhao Yue, Wanshun Xia, Qingqing Ding, Hongbin Bei, Yuefeng Gu, Ze Zhang
Format:	Article
Language:	English
Published:	MDPI AG 2023-11-01
Subjects:	oxidation low-cycle fatigue crack initiation single crystal superalloy
Online Access:	https://www.mdpi.com/2075-4701/13/11/1878