Role of MnS in the intergranular corrosion and depassivation of sensitized Type 304 stainless steel
Abstract During polarization in 1 M NaCl (pH 5.4), intergranular corrosion of sensitized re-sulfurized Type 304 stainless steel occurred after pit initiation at MnS inclusions. Intergranular corrosion occurred when the pitting corrosion reached a Cr-depleted region along the sensitized grain boundar...