Effect of Titanium Content on Mechanical Properties of Hot Rolled Plate of Nb-Ti Microalloying Q345A Steel

The  effect  of titanium  content  on  mechanical  properties  of  14～20  mm  hot  rolled plate  of Q345A  steel (0.08~0. 10C,1.19～1.46Mn,0.017～0.029Nb,0.02～0.08Ti) has  been studied. Results showed that as Ti=0.02%, the strength  of  steel  plate  was  not  obvious  change,as  Ti  content  was0.02～...