Effect of Nitrogen on the Corrosion Resistance of 6Mo Super Austenitic Stainless Steel
6Mo super austenitic stainless steel (SASS) with nitrogen contents of 0.2 and 0.4 (wt.%) was melted, and solution treatments at 1100, 1180, and 1250 °C for 30 min were performed. The effects of nitrogen on the microstructure and pitting resistance of the two steels that signed as 0.2N and 0.4N sampl...