A comparative study of the electrochemical corrosion behavior between Cr2N and CrN coatings

Thick Cr2N and CrN coatings were successfully prepared by arc ion plating (AIP) at a high deposition rate of more than 15 μm/h. The electrochemical corrosion behavior of Cr2N and CrN coatings in 3.5 wt% NaCl solution was investigated comparatively using potentiodynamic polarization and electrochemic...