Formation mechanism of recrystallisation internal friction peak and its application to determine the recrystallisation temperature of deformed pure Cu

The formation mechanism of a recrystallisation internal friction (IF) peak superimposed on a grain boundary (GB) IF peak for deformed copper was studied. The P1 peak, associated with the recrystallisation process, was observed at ∼ 599 K (2 K/min) during the first heating process. Subsequently, the...