Study on hydrogen-induced delayed cracking of steering shaft
A 17-4PH steering shaft in the ship was brittle fractured during service, and its chemical composition, microstructure, fracture morphology of the material, and force simulations were analyzed. The results show that the failure mode of the shaft is hydrogen-induced delayed cracking, and the crack so...