Development of High Nitrogen Austenite Stainless Steel 1Mn15Cr17Ni2N
0. 14C-0.35N austenite stainless steel 1Mn15Cr17Ni2N melted by 25t EAF-VOD+LF-680 kg ingot process. [N] was 0.040% and [O] was 0.0158% at end of VOD refining, and the analysis results indicated [N] 0. 139% and [0]0.0033% after nitrogen blown for 45 min in LF with blown nitrogen amount 50 m...