Effect of carbon content on the microstructure and phases of (Ti,V,Nb,Cr,Mo)Cx high-entropy carbide

High-entropy carbide (Ti,V,Nb,Cr,Mo)Cx with varying carbon content (x = 13â16 wt%) was synthesized using conventional argon sintering at 1800 °C. Homogeneous distribution of elements was obtained at x = 15 wt% of C, while the presence of residual secondary carbide was observed among all samples wit...

Full description

Bibliographic Details

Published in:	Proceedings of the Estonian Academy of Sciences
Main Authors:	Furqan Anwar, Marek Tarraste, Lutz-Michael Berger, Johannes Pötschke
Format:	Article
Language:	English
Published:	Estonian Academy Publishers 2025-04-01
Subjects:	high entropy carbide low temperature microstructure sintering routes
Online Access:	https://kirj.ee/wp-content/plugins/kirj/pub/proc-2-2025-132-136_20250416135448.pdf