Rapid solidification structure refinement mechanism in highly undercooled Cu based ternary alloys
Applying cycle superheating and molten glass purification technologies, Cu60Ni35Co5 alloys were deeply undercooled to maximum undercoolings of 284 K. The microstructure characteristics and its evolution varying with bulk undercooling during the rapidly solidified process were analyzed. It was found...