Magnetic softening of the Fe83Si3B11P2Cu1 amorphous/nanocrystalline alloys with large-size pre-existing α-Fe grains by high heating-rate annealing

The microstructure and soft magnetic properties of Fe83Si3B11P2Cu1 (at.%) nanocrystalline ribbons with different thicknesses up to 40 μm obtained by annealing the amorphous/nanocrystalline precursors at various heating rates (HRs) were studied. It was found that the thicker melt-spun alloy ribbons c...

Full description

Bibliographic Details

Published in:	Journal of Materials Research and Technology
Main Authors:	Yang Meng, Shujie Pang, Chuntao Chang, Guan Wang, Huyang Li, Tao Zhang
Format:	Article
Language:	English
Published:	Elsevier 2022-09-01
Subjects:	Fe-based alloy Nanocrystalline alloy Soft magnetic property Annealing
Online Access:	http://www.sciencedirect.com/science/article/pii/S2238785422010900