On Transformation and Stress–Strain–Temperature Behavior of Fine-Grained Ni-Rich NiTi Wire vs. Aging Mode
The present study was carried out using a cold-drawn wire of Ni<sub>50.8</sub>Ti at.% subjected to post-deformation solution treatment at 700 °C for 1 h to obtain a fine-grained recrystallized structure. Subsequent aging was carried out at a temperature range of 300, 430, and 500 °C for...