The influence of the heat treatment on delta ferrite transformation in austenitic stainless steel welds
Shielded metal arc (SMAW) welded specimens using austenitic consumable materials with different amount of delta-ferrite are annealed in range 650-750 °C through 2-10 hours. Factorial plan 3<sup>3</sup> with influenced factors regression analyze of measured delta-ferrite values is used. T...
| الحاوية / القاعدة: | Metalurgija |
|---|---|
| المؤلفون الرئيسيون: | , , |
| التنسيق: | مقال |
| اللغة: | الإنجليزية |
| منشور في: |
Croatian Society for Materials Protection
2012-04-01
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | http://hrcak.srce.hr/file/111123 |
| الملخص: | Shielded metal arc (SMAW) welded specimens using austenitic consumable materials with different amount of delta-ferrite are annealed in range 650-750 °C through 2-10 hours. Factorial plan 3<sup>3</sup> with influenced factors regression analyze of measured delta-ferrite values is used. The transformation i.e. decomposition of delta ferrite during annealing was analyzed regarding on weld cracking resistance using metallographic examination and WRC-1992 diagram. |
|---|---|
| تدمد: | 0543-5846 1334-2576 |