Effect of Bi on graphite morphology and mechanical properties of heavy section ductile cast iron
To improve the mechanical properties of heavy section ductile cast iron, bismuth (Bi) was introduced into the iron. Five castings with different Bi content from 0 to 0.014 wt.% were prepared; and four positions in the casting from the edge to the center, with different solidification cooling rates,...
Main Authors: | Song Liang, Guo Erjun, Tan Changlong |
---|---|
Format: | Article |
Language: | English |
Published: |
Foundry Journal Agency
2014-03-01
|
Series: | China Foundry |
Subjects: | |
Online Access: | http://www.foundryworld.com/uploadfile/2014041054209517.pdf |
Similar Items
-
Fatigue and Fracture Resistance of Heavy-Section Ferritic Ductile Cast Iron
by: Matteo Benedetti, et al.
Published: (2017-03-01) -
Effects of Silicon on Mechanical Properties and Fracture Toughness of Heavy-Section Ductile Cast Iron
by: Liang Song, et al.
Published: (2015-01-01) -
Influence of cooling rate and antimony addition content on graphite morphology and mechanical properties of a ductile iron
by: Liu Zhe, et al.
Published: (2012-05-01) -
Low temperature impact strength of heavy section ductile iron castings: effects of microstructure and chemical composition
by: C. Labrecque, et al.
Published: (2011-02-01) -
Performance of heavy ductile iron castings for windmills
by: Iulian Riposan, et al.
Published: (2010-05-01)