Mechanical properties and biocompatibility of polymer infiltrated sodium aluminum silicate restorative composites
Abstract A new type of polymer-infiltrated-ceramic-network composites (PICNs) was fabricated by infiltrating methacrylate-based monomers into partially sintered porous ceramics. The mechanical properties (flexural strength, flexural modulus, elastic modulus, Vickers hardness, fracture toughness) wer...
Main Authors: | Huining Wang, Bencang Cui, Jing Li, Shu Li, Yuanhua Lin, Deping Liu, Ming Li |
---|---|
Format: | Article |
Language: | English |
Published: |
SpringerOpen
2017-03-01
|
Series: | Journal of Advanced Ceramics |
Subjects: | |
Online Access: | http://link.springer.com/article/10.1007/s40145-016-0214-0 |
Similar Items
-
Mechanical and biocompatible properties of polymer-infiltrated-ceramic-network materials for dental restoration
by: Bencang Cui, et al.
Published: (2020-02-01) -
Preparation and Characterization of Sodium Aluminum Silicate-Polymer Composites and Effects of Surface Roughness and Scratch Directions on Their Flexural Strengths
by: Bencang Cui, et al.
Published: (2021-04-01) -
Evaluating Fracture Resistance And Failure Modes Of Root Filled Teeth Restored With CAD/CAM-Fabricated Post And Core
by: Alkhatri R, et al.
Published: (2019-11-01) -
Longevity of Polymer-Infiltrated Ceramic Network and Zirconia-Reinforced Lithium Silicate Restorations: A Systematic Review and Meta-Analysis
by: William Banh, et al.
Published: (2021-09-01) -
Biomechanical properties of polymer-infiltrated ceramic crowns on one-piece zirconia implants after long-term chewing simulation
by: Pia Baumgart, et al.
Published: (2018-05-01)