Summary: | In this work, we propose a polymorphic method for the quantitative analysis in zirconia. This procedure uses a square system of equations relating the intensities of a peaks groups set in the diffraction pattern with the weight fractions of the different phases present in the sample. In this system it is used as unknowns, besides the relative abundance of the phases, a group of parameters that incorporates the contribution from the tails of the groups adjacent to the intensity of a selected group. The described procedure has been applied to a simulated diffractogram corresponding to a composition of zirconia of 50% of cubic phase, 25% of tetragonal phase and 25% of monoclinic phase, and also to a sample of zirconia processed by the sol-gel method.<br><br>En este trabajo se propone un método polimórfico para el análisis cuantitativo de fases en la circona. Este procedimiento emplea un sistema de ecuaciones compatible y determinado que relaciona las intensidades de un conjunto de grupos de picos del espectro de difracción con las fracciones en peso de las diferentes fases presentes en la muestra. En dicho sistema, además de las abundancias relativas de las fases, se utilizan como incógnitas un conjunto de parámetros que dan cuenta de la aportación de las colas de los grupos de picos adyacentes al grupo de picos considerado. Este procedimiento se ha aplicado a un difractograma simulado correspondiente a una circona con 50% de fase cúbica, 25% de fase tetragonal y 25% de fase monoclínica y también a una muestra en polvo de circona fabricada mediante técnicas sol-gel.
|