The effect of pre-heating and pre-cold treatment on the formation of liquation and solidification cracks of nickel-based superalloy welded by laser beam
The present study has evaluated the solidification and liquation cracks of GTD-111 superalloy by pulsed Nd:YAG laser techniques. For this purpose, samples were subjected to different temperatures under the conditions of heat treatment (1120, 1200 and, 1230 °C), pre-cooling (−30 and 0 °C), and pre-he...
Main Authors: | Zhuoyi Chen, Morteza Taheri |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2020-09-01
|
Series: | Journal of Materials Research and Technology |
Subjects: | |
Online Access: | http://www.sciencedirect.com/science/article/pii/S2238785420315428 |
Similar Items
-
Suppression of liquation cracking susceptibility via pre-weld heat treatment for manufacturing of CM247LC superalloy turbine blade welds
by: Eun-Joon Chun, et al.
Published: (2021-11-01) -
Predicting Susceptibility to Solidification Cracking and Liquation Cracking by CALPHAD
by: Sindo Kou
Published: (2021-09-01) -
The Evolution of Cast Microstructures on the HAZ Liquation Cracking of Mar-M004 Weld
by: Yi-Hsin Cheng, et al.
Published: (2018-01-01) -
Liquation Cracking Tendency of Novel Al-Mg-Zn Alloys with a Zn/Mg Ratio below 1.0 during Fusion Welding
by: Di Zhang, et al.
Published: (2020-02-01) -
Research on the Grain Boundary Liquation Mechanism in Heat Affected Zones of Laser Forming Repaired K465 Nickel-Based Superalloy
by: Qiuge Li, et al.
Published: (2016-03-01)