Efecto de la ceniza volante en las propiedades mecánicas de concretos hechos con agregado calizo triturado de alta absorción

• Main Authors: J. A. Canul, E. I. Moreno, J. M. Mendoza Rangel
• Format: Article
• Language: English
• Published: Asociación Latinoamericana de Control de Calidad, Patología y Recuperación de la Construcción 2016-09-01
• Series: Revista ALCONPAT
• Subjects: ceniza volante; agregado calizo; absorción; resistencia a la compresión; módulo de elasticidad
• Online Access: https://revistaalconpat.org/index.php/RA/article/view/150

Efecto de la ceniza volante en las propiedades mecánicas de concretos hechos con agregado calizo triturado de alta absorción RESUMEN El concreto elaborado con agregado calizo triturado de alta absorción de Yucatán, México, es considerado de baja calidad. El objetivo de la investigación es mejorar las propiedades mecánicas del concreto elaborado con este tipo de agregado incorporando ceniza volante (CV). Las propiedades medidas fueron: Resistencia a la compresión (RC) y módulo de elasticidad. Se utilizaron relaciones agua/cemento de 0.5 y 0.7, la CV se incorporó como sustitución parcial del cemento en un 20% y 40%, y como aditivo mineral en un 10% y 20%. Los resultados indican que la CV puede ser utilizada en concretos con ACTAA como agregado inerte fino ya que logra mantener una RC similar a la referencia. Se presentan ecuaciones para la predicción de propiedades mecánicas. Palabras clave: ceniza volante; agregado calizo; absorción; resistencia a la compresión; módulo de elasticidad.   Fly ash effect on mechanical properties of concretes made with high absorbent crushed limeston aggregates ABSTRACT Concrete made with high-absorbent crushed limestone aggregates from Yucatán, México are well known as a low quality concrete. The aim of this investigation is to enhance the mechanical properties of concrete with high absorbent crushed limestone aggregates and fly ash. The measured properties were: compressive strength and elastic modulus. The water/cement ratios were 0.5 and 0.7, fly ash was incorporated as partial substitution of cement with 20% and 40% and as a mineral additive in 10% and 20%. Results show that fly ash can be used in this kind of concretes as mineral additive due to compressive strength was similar to those reference samples. Finally, an equation for predicting mechanical properties is reported. Keywords: fly ash; limestone aggregates; absorption; compressive strength; elastic modulus.   Efeito de cinzas volantes nas propriedades mecânicas de concreto feitos com agregado calcário moído de alta absorção RESUMO O concreto produzido com agregado calcário de alta absorção de Yucatan, no México, é considerado de baixa qualidade. O objetivo deste estudo é o de melhorar as propriedades mecânicas do concreto fabricado com este tipo de agregado incorporando cinza volante (CV). As propriedades medidas foram: resistência à compressão (RC) e módulo de elasticidade. Foram utilizadas relações água/cimento de 0,5 e 0,7, a CV foi incorporada como substituição parcial de cimento em 20% e 40%, e como um aditivo mineral a 10% e 20%. Os resultados indicam que a CV pode ser usada nesses concretos como um agregado miúdo inerte, pois apresenta uma resistência à compressão similar a amostra de referência. São apresentadas equações para a previsão das propriedades mecânicas. Palavras chave: cinzas volantes; agregados de calcário; absorção; resistência à compressão; módulo de elasticidade.