| Summary: | The introduction of<b> </b>multi-walled carbon nanotubes (MWCNTs) into polymer matrixes has been an important tool to alter and improve some properties in polymer nanocomposites, including biodegradable polymers such as poly(3-hydroxybutyrate-<i>co</i>-3-hydroxyvalerate) (PHBV). In this work, PHBV nanocomposites with 0.05, 0.50, 1.00, 1.50 and 2.00 wt % of MWCNTs were produced by solvent casting. MWCNT morphology and structure were characterized by Raman spectroscopy, and transmission electron microscopy (TEM). It was observed that MWCNTs have a considerable amount of amorphous carbon (AC) onto their surface and a wide distribution of the tube diameter. MWCNTs act as the nucleating agent in the PHBV matrix, as verified by differential scanning calorimetry (DSC). Thermogravimetric analysis (TGA) showed that thermal stability was not significantly affected. The nanofiller dispersion into the PHBV matrix was not effective for concentrations from 1 wt % according to the micrographs obtained in scanning electron microscopy (SEM). The contact angle was changed with the introduction of MWCNTs, turning the nanocomposites hydrophobic and improving the mechanical tensile properties of the PHBV matrix.
|
|---|