Contamination Study of Zirconia on the Densification Process and Properties of Transparent MgAl2O4 Ceramics
In this paper, transparent magnesium aluminate (MgAl2O4) spinel ceramics are fabricated through pressureless sintering combined with hot isostatic pressing (HIPing). To investigate the effect of zirconia on sintering behavior, microstructure, and optical properties of transparent spinel ceramics, di...
Main Authors: | Yi Li, Qun Zeng, Jian Zhang, Dan Han, Shiwei Wang |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2019-03-01
|
Series: | Materials |
Subjects: | |
Online Access: | http://www.mdpi.com/1996-1944/12/5/749 |
Similar Items
-
Manufacturing Optically Transparent Thick Zirconia Ceramics by Spark Plasma Sintering with the Use of Collector Pressing
by: Vladimir Paygin, et al.
Published: (2021-02-01) -
Grain size influence on the thermal properties of stabilized zirconia-nano spinel (Al2O3-MgO) composites
by: mohammad Almasi Kashi, et al.
Published: (2019-10-01) -
Frittage micro-ondes du matériau spinelle MgAl2O4 : vers des céramiques transparentes
by: Macaigne, Rodolphe
Published: (2017) -
Synthesis of Hercynite under Air Atmosphere using MgAl2O4 Spinel
by: Sasan Otroj
Published: (2015-06-01) -
Characterization of MgAl2O4 sintered ceramics
by: Obradović Nina, et al.
Published: (2019-01-01)