Summary: | In this study, a magnesium oxide (MgO) coated corncob biochar (MCB) was synthesized by pyrolyzing MgCl2 pretreated corncob, for a better performance in lead immobilization in a contaminated soil compared with corncob biochar (CB). The properties and microstructures of CB and MCB were investigated. It was observed that MgO particles ranging from 1 to 2 μm were well coated on MCB, and the MgO content in MCB was calculated at 29.90% in w/w. The surface area of the biochar was significantly enhanced from 0.07 to 26.56 m2/g after the MgO coating. The MgO coating also significantly facilitated the lead removal percentage from 23% to 74% in aqueous solution by biochar. CB failed to immobilize lead in a soil washing residue and could not reduce its environmental risks in a laboratory incubation study. In contrast, MCB was applied to the soil and resulted in a significant reduction in TCLP leached lead from 10.63 to 5.24 mg/L (reduced by 50.71%). The comparison between MCB and other amendments suggests that the biochar component of MCB adsorbed lead onto its surface through cation-π interaction and increased surface adsorption due to higher surface area, and then the MgO coated on MCB's surface further enhanced the adsorption through precipitation. The synergistic roles of biochar-mineral composites make them a promising candidate for soil remediation. Keywords: Engineered biochar, Magnesium oxide (MgO), Biochar-mineral composite, Lead immobilization, In situ stabilization, Soil remediation
|