Structure and Characterization of TiC/GLC Multilayered Films with Various Bilayers Periods
The spontaneously self-organizing multilayered graphite-like carbon (denoted as GLC) /TiC films with various bilayer periods in the range of 13.3–17.5 nm were deposited on silicon and 1Cr18Mn8Ni5N stainless steel substrates using closed field magnetron sputtering deposition facility. The microstruct...
Main Authors: | Weiqi Wang, Xiaoming Ling, Rui Wang, Wenhao Nie, Li Ji, Hongxuan Li |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2021-06-01
|
Series: | Coatings |
Subjects: | |
Online Access: | https://www.mdpi.com/2079-6412/11/7/787 |
Similar Items
-
Tribology of multilayer coatings for wear reduction: A review
by: Mahdi Khadem, et al.
Published: (2017-09-01) -
Microstructure, mechanical and tribological properties of multilayer Ti-DLC thick films on Al alloys by filtered cathodic vacuum arc technology
by: Hongshuai Cao, et al.
Published: (2021-01-01) -
High-Temperature Tribological Performance of Hard Multilayer TiN-AlTiN/nACo-CrN/AlCrN-AlCrO-AlTiCrN Coating Deposited on WC-Co Substrate
by: Asad Alamgir, et al.
Published: (2020-09-01) -
The Tribological Investigations of Multicomponent Multilayered Ion-Plasma Coatings Avinit
by: A. Sagalovych, et al.
Published: (2011-06-01) -
Environmental Molecular Effect on the Macroscale Friction Behaviors of Graphene
by: Panpan Li, et al.
Published: (2021-06-01)