The Formation Mechanism of Cu(In0.7Ga0.3)Se2 Nanoparticles and the Densification Trajectory of the Se-Rich Quaternary Target by Hot Pressing
In this paper, a method to obtain the CuInGaSe2 (CIGS) absorber layer with an appropriate selenium content is put forward, in which a Se-rich target is used to deposit a CIGS thin-film and this film is annealed in a Se-free inert atmosphere. The key issue of this method is the preparation of a Se-ri...
Main Authors: | Qiang Ma, Weijia Zhang, Zhaoyi Jiang, Denghao Ma, Yulong Zhang, Chaoqun Lu, Zhiqiang Fan |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2018-03-01
|
Series: | Crystals |
Subjects: | |
Online Access: | http://www.mdpi.com/2073-4352/8/3/135 |
Similar Items
-
CuIn0.7Ga0.3Se2 thin films’ properties grown by close-spaced vapor transport technique for second-generation solar cells
by: N. Oulmi, et al.
Published: (2019-08-01) -
Investigation of Approaches to Control the Compositions of Zn(Se,OH) Buffers Prepared by Chemical Bath Deposition Process for Cu(In,Ga)Se2 (CIGS) Solar Cells
by: Chia-Hua Huang, et al.
Published: (2018-08-01) -
Termal Buharlaştırma Yöntemiyle Hazırlanan Ga Katkılı CuInSe2 İnce Filmlerin Yapısal Özelliklerinin İncelenmesi
by: Murat KALELİ, et al.
Published: (2017-11-01) -
Progress on Low-Temperature Pulsed Electron Deposition of CuInGaSe2 Solar Cells
by: Massimo Mazzer, et al.
Published: (2016-03-01) -
How the Starting Precursor Influences the Properties of Polycrystalline CuInGaSe2 Thin Films Prepared by Sputtering and Selenization
by: Greta Rosa, et al.
Published: (2016-05-01)