Effect of Local Recrystallized Grains on the Low Cycle Fatigue Behavior of a Nickel-Based Single Crystal Superalloy
This paper aims to understand the effect of local recrystallization (RX) on the low cycle fatigue fracture of a turbine-blade single crystal nickel-based superalloy. The fatigue life of the single crystal superalloy was evidently decreased by local recrystallization. In single crystal specimens, cas...
Main Authors: | Xianfeng Ma, Jishen Jiang, Wenjie Zhang, Hui-ji Shi, Jialin Gu |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2019-06-01
|
Series: | Crystals |
Subjects: | |
Online Access: | https://www.mdpi.com/2073-4352/9/6/312 |
Similar Items
-
Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 °C by In Situ SEM Studies
by: Hao Yang, et al.
Published: (2020-07-01) -
Effect of recrystallization on axial high cycle fatigue properties of DD6 single crystal superalloy
by: HAN Mei, et al.
Published: (2019-06-01) -
Integrated TEM/transmission-EBSD for recrystallization analysis in nickel-based disc superalloy
by: Fei Sun
Published: (2021-02-01) -
Recrystallization behavior of the fourth generation single crystal superalloy based on different original microstructure preset strain
by: SHI Zhen-xue, et al.
Published: (2019-05-01) -
Experimental and Numerical Studies on Recrystallization Behavior of Single-Crystal Ni-Base Superalloy
by: Runnan Wang, et al.
Published: (2018-07-01)