| Summary: | This paper aims to evaluate the applicability of volcanic mud as the fine aggregate for controlled low-strength material (CLSM) by the experimental method. Two types of binder were selected, including cement and alkali-activated slag binders (without cement). The study mainly explored the effects of different addition rates of volcanic mud and different concentrations of alkaline agents (sodium hydroxide) on the engineering properties of CLSM. The test results show that the CLSMs with cement and volcanic mud have better workability and less water bleeding. However, the compressive strength of CLSM decreases as the replacement rate of volcanic mud increases, and the setting time also increases. The replacement rate of volcanic mud is recommended to be 20%. The volcanic mud mixed with the alkali-activated slag binder (without cement) can be successfully made into CLSM. When the concentration of sodium oxide in CLSM is 5%, although the compressive strength is highest at 7 days or 28 days, it cannot be hardened at the early age (before four days) and without compressive strength. CLSM with 20% sodium oxide concentration has poor workability. Its compressive strength is slightly lower than that of the 10% group. Therefore, the amount of calcium hydroxide recommended is 10%.
|
|---|