3 kW 20/400 Yb-Doped Aluminophosphosilicate Fiber With High Stability
By using the MCVD system and the all-gas-phase chelate precursor doping technique, we fabricated an Yb-doped aluminophosphosilicate fiber with 20 μm-core and 400 μm-clad in diameter, i.e., 20/400 Yb-APS fiber. The fiber core was doped with 1100 ppm Yb<sup>3+</sup>,...
Main Authors: | Shuang Liu, Kun Peng, Huan Zhan, Li Ni, Xiaolong Wang, Yuying Wang, Yuwei Li, Juan Yu, Lei Jiang, Rihong Zhu, Jianjun Wang, Feng Jing, Aoxiang Lin |
---|---|
Format: | Article |
Language: | English |
Published: |
IEEE
2018-01-01
|
Series: | IEEE Photonics Journal |
Subjects: | |
Online Access: | https://ieeexplore.ieee.org/document/8423065/ |
Similar Items
-
Yb-Doped Aluminophosphosilicate Triple-Clad Laser Fiber With High Efficiency and Excellent Laser Stability
by: Shuang Liu, et al.
Published: (2019-01-01) -
Fiber Design and Fabrication of Yb/Ce Codoped Aluminosilicate Laser Fiber With High Laser Stability
by: Yuwei Li, et al.
Published: (2018-01-01) -
Air-Core Ring Fiber Guiding >400 Radially Fundamental OAM Modes Across S + C + L Bands
by: Yingning Wang, et al.
Published: (2021-01-01) -
Enhancement of Tetrahedral Chromium (Cr<sup>4+</sup>) Concentration for High-Gain in Single-Mode Crystalline Core Fibers
by: Chun-Nien Liu, et al.
Published: (2020-01-01) -
Optical Properties of Chromium and Erbium Co-Doped Alumina–Germania–Calcia–Yttria–Silica Based Fiber
by: Alexander V. Kir'yanov, et al.
Published: (2019-01-01)