| Summary: | Pineapple leaf fiber (PLF) is one of the natural fibers that abundantly can be found in Malaysia, but the usage of the pineapple plant is limited only on their fruit and the other parts to be a waste. In this study, PLF is used as the reinforcement material and starch (SH) used as the matrix or binder. Both materials were combined with several compositions ratio (weight percentage) of PLF/SH composites which are 50PLF/50SH, 60PLF/40SH and 70PLF/30SH. Before undergo the fabrication process, the fiber has gone through an alkaline treatment to increase the strength of the fiber and chopped with an approximate size range from 0.5 mm to 5 mm. Besides that, SH powder is sieved to gain several particulate sizes which are 75 μm, 100 μm and 250 μm. The related tests such as flexural, hardness, density tests and macrostructure analysis have been done to determine their mechanical properties of composite. Based on the results, the sample with composition of 70PL/30SH with 75 μm has shown the highest result for flexural stress which is 14.49 MPa. While, the composite with the same composition of 70PLF/30SH with particulate size SH of 250 μm has shown the highest result in the hardness of 67 Shore-D and density of 1.36 g/cm3 respectively.
|
|---|