| Summary: | This work is devoted to the study of the time and temperature dependence of the static grain growth in YTZP 4 mol %, with an average grain size within the submicrometric range ( d> 0.1 μm). Also, the mechanical response in the temperature interval between 1200 ºC and 1500 ºC is analysed. The grain growth is controlled by the yttria segregation at the grain boundaries, which plays a key role in the cationic diffusion processes. Microstructural characterization of both as-received and deformed samples allows to conclude that plastic deformation is due to grain boundary sliding (GBS), with stress exponents increasing with the flow stress, but in all cases they are lower than n = 2.<br><br>En este trabajo se estudia la dependencia temporal y con la temperatura del crecimiento estático del tamaño de grano en YTZP 4 mol %, con un tamaño inicial dentro del rango submicrométrico ( mayor que 0.1 μm), así como su comportamiento mecánico a temperaturas comprendidas entre 1200 ºC y 1500 ºC. El crecimiento de grano está controlado por la segregación de itrio en las fronteras de éstos, la cual juega un papel determinante en los procesos de difusión catiónica. La caracterización microestructural de las muestras, antes y después de ser deformadas, nos permite concluir que la deformación del material es debida al deslizamiento de fronteras de grano (DFG), con exponentes de tensión que aumentan con la tensión de deformación, siendo siempre inferiores a n = 2.
|
|---|