Fabrication of Pore-Selective Metal-Nanoparticle-Functionalized Honeycomb Films via the Breath Figure Accompanied by In Situ Reduction

• Main Authors: Yongjiang Li, Xiaoyan Ma, Jingyu Ma, Zongwu Zhang, Zhaoqi Niu, Fang Chen
• Format: Article
• Language: English
• Published: MDPI AG 2021-01-01
• Series: Polymers
• Subjects: honeycomb films; POSS-based star-shaped polymers; pore-selective functionalization; metal nanoparticles; breath figure
• Online Access: https://www.mdpi.com/2073-4360/13/3/316

Honeycomb films pore-filled with metal (Au, Ag, and Cu) nanoparticles were successfully prepared by combining the breath figure method and an in situ reduction reaction. First, a polyhedral oligomeric silsesquioxane (POSS)-based star-shaped polymer solution containing metal salt was cast under humid conditions for the formation of honeycomb films pore-filled with metal salt through the breath figure method. The morphology of the honeycomb films was mainly affected by the polymer molecular structure and the metal salt. Interestingly, the promoting effect of the metal salt in the breath figure process was also observed. Then, honeycomb films pore-filled with metal nanoparticles were obtained by in situ reduction of the honeycomb films pore-filled with metal salt using NaBH₄. Notably, the metal nanoparticles can be selectively functionalized in the pores or on the surface of the honeycomb films by controlling the concentration of the NaBH₄. Metal-nanoparticle-functionalized honeycomb films can prospectively be used in catalysis, flexible electrodes, surface-enhanced Raman spectroscopy (SERS), and wettability patterned surfaces.