Machinability of INCONEL718 Alloy with a Porous Microstructure Produced by Laser Melting Powder Bed Fusion at Higher Energy Densities
Products produced by additive manufacturing (AM) seek to exploit net shape manufacturing by eliminating or minimizing post-process stages such as machining. However, many applications which include turbo machinery components with tight dimensional tolerances and a smooth surface finish will require...
Main Authors: | Paul Wood, Antonio Díaz-Álvarez, José. Díaz-Álvarez, María Henar Miguélez, Alexis Rusinek, Urvashi F. Gunputh, Gavin Williams, Slim Bahi, Judyta Sienkiewicz, Paweł Płatek |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-12-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/13/24/5730 |
Similar Items
-
Microstructure and machinability evaluation in micro milling of selective laser melted Inconel 718 alloy
by: Hansong Ji, et al.
Published: (2021-09-01) -
High strain rate effect on tensile ductility and fracture of AM fabricated Inconel 718 with voided microstructures
by: P. Wood, et al.
Published: (2021-10-01) -
Impact of laser scanning speed on microstructure and mechanical properties of Inconel 718 alloys by selective laser melting
by: Hong-ying Wang, et al.
Published: (2021-05-01) -
Formability, Microstructure and Properties of Inconel 718 Superalloy Fabricated by Selective Laser Melting Additive Manufacture Technology
by: Xiaoping Liu, et al.
Published: (2021-02-01) -
The impact of laser control on the porosity and microstructure of selective laser melted nickel superalloy 718
by: Travis E. Shelton, et al.
Published: (2021-09-01)