Crack growth of explosive welding zirconium-steel bimetal subjected to cyclic bending
The paper presents the fatigue test results including the cracks growth in the composite zirconium-steel subjected to oscillatory bending. Specimens of square cross-section without melted layer and with a melted layer were tested. In the specimens the net ratio of thickness of steel to zirconium la...
Main Authors: | , |
---|---|
Format: | Article |
Language: | English |
Published: |
Gruppo Italiano Frattura
2017-09-01
|
Series: | Frattura ed Integrità Strutturale |
Subjects: | |
Online Access: | https://www.fracturae.com/index.php/fis/article/view/1925 |
id |
doaj-58ae0917da834aa89c28802450248f3b |
---|---|
record_format |
Article |
spelling |
doaj-58ae0917da834aa89c28802450248f3b2021-01-29T17:14:43ZengGruppo Italiano FratturaFrattura ed Integrità Strutturale1971-89932017-09-01114210.3221/IGF-ESIS.42.05Crack growth of explosive welding zirconium-steel bimetal subjected to cyclic bendingD. Rozumek0Z. Marciniak1Opole University of Technology, PolandOpole University of Technology, Poland The paper presents the fatigue test results including the cracks growth in the composite zirconium-steel subjected to oscillatory bending. Specimens of square cross-section without melted layer and with a melted layer were tested. In the specimens the net ratio of thickness of steel to zirconium layers was h1 : h2 = 2.5 : 1. It was observed that a higher fraction of the intermetallic inclusions near the interface increase the fatigue life. Two different interaction mechanisms between a crack and interface were observed. https://www.fracturae.com/index.php/fis/article/view/1925Explosive weldingBendingFatigue crack growthJoint |
collection |
DOAJ |
language |
English |
format |
Article |
sources |
DOAJ |
author |
D. Rozumek Z. Marciniak |
spellingShingle |
D. Rozumek Z. Marciniak Crack growth of explosive welding zirconium-steel bimetal subjected to cyclic bending Frattura ed Integrità Strutturale Explosive welding Bending Fatigue crack growth Joint |
author_facet |
D. Rozumek Z. Marciniak |
author_sort |
D. Rozumek |
title |
Crack growth of explosive welding zirconium-steel bimetal subjected to cyclic bending |
title_short |
Crack growth of explosive welding zirconium-steel bimetal subjected to cyclic bending |
title_full |
Crack growth of explosive welding zirconium-steel bimetal subjected to cyclic bending |
title_fullStr |
Crack growth of explosive welding zirconium-steel bimetal subjected to cyclic bending |
title_full_unstemmed |
Crack growth of explosive welding zirconium-steel bimetal subjected to cyclic bending |
title_sort |
crack growth of explosive welding zirconium-steel bimetal subjected to cyclic bending |
publisher |
Gruppo Italiano Frattura |
series |
Frattura ed Integrità Strutturale |
issn |
1971-8993 |
publishDate |
2017-09-01 |
description |
The paper presents the fatigue test results including the cracks growth in the composite zirconium-steel subjected to oscillatory bending. Specimens of square cross-section without melted layer and with a melted layer were tested. In the specimens the net ratio of thickness of steel to zirconium layers was h1 : h2 = 2.5 : 1. It was observed that a higher fraction of the intermetallic inclusions near the interface increase the fatigue life. Two different interaction mechanisms between a crack and interface were observed.
|
topic |
Explosive welding Bending Fatigue crack growth Joint |
url |
https://www.fracturae.com/index.php/fis/article/view/1925 |
work_keys_str_mv |
AT drozumek crackgrowthofexplosiveweldingzirconiumsteelbimetalsubjectedtocyclicbending AT zmarciniak crackgrowthofexplosiveweldingzirconiumsteelbimetalsubjectedtocyclicbending |
_version_ |
1724318715649982464 |