Study on microstructure and mechanical properties of P92 steel after high-temperature long-term aging at 650°C
A series of long-term high-temperature aging tests of ASME A335-P92 steel from 1,000 to 29,000 h at 650°C were carried out. The microstructure evolution of as-received and aging specimens at different stages was investigated using optical microscope observations, scanning electron microscope examina...
Main Authors: | , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
De Gruyter
2020-10-01
|
Series: | High Temperature Materials and Processes |
Subjects: | |
Online Access: | https://doi.org/10.1515/htmp-2020-0087 |
Summary: | A series of long-term high-temperature aging tests of ASME A335-P92 steel from 1,000 to 29,000 h at 650°C were carried out. The microstructure evolution of as-received and aging specimens at different stages was investigated using optical microscope observations, scanning electron microscope examinations, and TEM investigations. The static mechanical strength properties (yield strength/ultimate tensile strength) at room and 600°C test temperatures and the plastic performance (elongation/reduction in area) were also analyzed. The experimental results show that the Laves phase can be precipitated rapidly in the early aging period. After a certain aging period, the continuous precipitation of M23C6 and the relatively high coarsening rate of Laves resulted in a rapid decrease of room and high-temperature mechanical properties in the early aging period. However afterwards for the long aging time, a slow decline in tendency of mechanical properties was presented. |
---|---|
ISSN: | 0334-6455 2191-0324 |