Study on microstructure and mechanical properties of P92 steel after high-temperature long-term aging at 650°C
A series of long-term high-temperature aging tests of ASME A335-P92 steel from 1,000 to 29,000 h at 650°C were carried out. The microstructure evolution of as-received and aging specimens at different stages was investigated using optical microscope observations, scanning electron microscope examina...
Main Authors: | Duan Peng, Liu Zongde, Li Bin, Li Jiayao, Tao Xiangqian |
---|---|
Format: | Article |
Language: | English |
Published: |
De Gruyter
2020-10-01
|
Series: | High Temperature Materials and Processes |
Subjects: | |
Online Access: | https://doi.org/10.1515/htmp-2020-0087 |
Similar Items
-
Effect of cooling modes after austenitization on stabilities of microstructure and hardness of P92 steel aged at 650℃
by: ZHONG Jiao, et al.
Published: (2019-01-01) -
Forecasting the Particle Diameter Size Distribution in P92 (X10CrWMoVNb9-2) Steel After Long-Term Ageing at 600 and 650 °C
by: Zieliński A., et al.
Published: (2016-06-01) -
Changes In Properties and Microstructure of High-Chromium 9-12%Cr Steels Due to Long-Term Exposure at Elevated Temperature
by: Zieliński A., et al.
Published: (2016-06-01) -
Influence of Thermal Ageing on Microstructure and Tensile Properties of P92 Steel
by: Sakthivel T., et al.
Published: (2018-04-01) -
Microstructure and Mechanical Properties of Heat-treated T92 Martensitic Heat Resistant Steel
by: Rajesh Kannan P., et al.
Published: (2017-09-01)