| Summary: | In this paper, the influence of welding speed on tensile properties of AA2024-T3 fibre laser welds was investigated by monitoring the deformation behaviour during tensile loading. In-situ micro-tensile testing combined with a high-resolution optical microscope and DIC was used to measure strain distribution in narrow weld regions showing characteristics of fibre laser beam welding with limited metallurgical modifications. A chemical etching technique was used to generate a micro-scale random speckle pattern by revealing the weld microstructure. Such pattern enabled a sufficient spatial resolution of strain while keeping the weld seam visible during deformation. The results of microstructural and mechanical properties determined under numerous welding speeds indicated that increasing the welding speed led to the transition of weld pool shape from circular to elliptical to teardrop with a greater fraction of equiaxed dendrites. The weaker strength of the weld, as measured by local lower micro-hardness values, constrained significant plasticity development locally within the weld. Tensile tests revealed that increasing the welding speed resulted in greater yield strength and ultimate tensile strength, whereas, total elongation to failure dropped. The tensile properties improved with increasing welding speed as the fraction of equiaxed dendrites increased. Keywords: Aluminium alloy, Fibre laser welding, Digital image correlation, Joining, Microstructure
|
|---|