Physical, chemical and mechanical properties of Pinus sylvestris wood at five sites in Portugal

• Main Authors: Fernandes C, Gaspar MJ, Pires J, Alves A, Simões R, Rodrigues JC, Silva Maria E, Carvalho A, Brito José E, Lousada José L
• Format: Article
• Language: English
• Published: Italian Society of Silviculture and Forest Ecology (SISEF) 2017-08-01
• Series: iForest - Biogeosciences and Forestry
• Subjects: Bending Tests; Correlations; Mechanical Traits; NIR Spectrometry; Scots Pine; Wood-Density Components; Wood Quality; X-ray Microdensitometry
• Online Access: https://iforest.sisef.org/contents/?id=ifor2254-010
• ISSN: 1971-7458; 1971-7458

The reduction of resinous species in Portuguese forest areas has caused constraints to wood industry supplies. Portugal represents the extreme southwest of Scots pine (Pinus sylvestris) natural distribution and large gaps exist in the knowledge of its wood-quality characteristics. Understanding the relationship between these traits is important for recognizing which combination of wood properties is the most suitable for specific uses. To address these questions, we assessed wood-quality traits, namely, wood-density components (microdensitometric analysis), chemical composition (NIR spectrometry) and mechanical properties (bending tests) of wood samples collected at five representative forest sites in Portugal. Our results showed that Portuguese Pinus sylvestris has good radial growth and denser wood, higher extractive content and higher stiffness and strength than northern European provenances. The lignin content was within the range attributed to softwoods. Among the Portuguese stands, trees growing at lower-altitude sites exhibited denser wood and higher mechanical properties, while trees from high-elevations showed higher amounts of lignin. Ring density was more strongly correlated with earlywood than latewood density. A negative, non-significant correlation was found between ring density and width, supporting the assumption that the higher radial growth (ring width) does not negatively affect wood quality (density). In general, chemical properties had a weak relationship with physical and mechanical properties (MOE and MOR). Both mechanical traits were positively correlated with density and growth components, supporting the assumption that trees with high radial growth do not exhibit poorer mechanical performances.