Comprehensive Understanding of Hillocks and Ion Tracks in Ceramics Irradiated with Swift Heavy Ions
Amorphizable ceramics (LiNbO<sub>3</sub>, ZrSiO<sub>4</sub>, and Gd<sub>3</sub>Ga<sub>5</sub>O<sub>12</sub>) were irradiated with 200 MeV Au ions at an oblique incidence angle, and the as-irradiated samples were observed by transmission ele...
Main Authors: | Norito Ishikawa, Tomitsugu Taguchi, Hiroaki Ogawa |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2020-12-01
|
Series: | Quantum Beam Science |
Subjects: | |
Online Access: | https://www.mdpi.com/2412-382X/4/4/43 |
Similar Items
-
Raman Spectra and Microstructure of Zinc Oxide irradiated with Swift Heavy Ion
by: Yin Song, et al.
Published: (2019-07-01) -
Swift heavy ion irradiation of polyester and polyolefin polymeric film for gas separation application
by: Adeniyi, Olushola Rotimi
Published: (2016) -
Investigation of Ion Irradiation Effects in Silicon and Graphite Produced by 23 MeV I Beam
by: Kristina Tomić Luketić, et al.
Published: (2021-04-01) -
Review of Swift Heavy Ion Irradiation Effects in CeO<sub>2</sub>
by: William F. Cureton, et al.
Published: (2021-06-01) -
MD and TEM evaluation of swift Xe ion induced latent tracks in Si3N4
by: R.A. Rymzhanov, et al.
Published: (2019-12-01)