Studi tentang standar sepatu kanvas untuk ekspor

• Main Author: Sri Bandi
• Format: Article
• Language: English
• Published: Center for Leather, Rubber, and Plastics 1992-04-01
• Series: Majalah Kulit, Karet, dan Plastik
• Online Access: http://ejournal.kemenperin.go.id/mkkp/article/view/475/451

In this study, 10 pairs of canvas shoes with rubber soles of various trade marks were tested. The samples were iaken either from manufacturers or markets in DKI Jakarta or DIY, the test methd used was as stated in sII 1406-g5. The objective of this study is to compile a concept of standard for export quality canvas shoes. The test results of canvas with rubber soles can be provided as follows the portion - bursting strengrh (15,839 - 22,4737) kg/cm'; breaking load of shoe taces 463,31 - &3,846 N; the bottom portion - the thickness of soles without treat (1,31 - z,7g) mm; tensile strength (6,25 - 11,94) N/mm2; elongation at break (202,45 - 522,93)Vo; permanent set 50 qo e,46 - 5,22); specific gravity (1,L5 - 1,29); Grasselli abrasion resistance (0,49 - 3,25) mmTkgm; tear strength (2,4g -6,46) N/ mm2; flexing resistance no cracks permitted ; hardness (54,17 - 72,g6) shore A. The 10 pairs ofcanvas shoes were also visually inspected according to sII 1406 - 85 and they fulfilled the requirements. Besides testing some standards concepts from other countries such as JIS (Japanese Industrial Standard), IS (Indian standard), CNS (china National Standard), KS (Korean standard) were also studied and based on them, a conclusion can be drawn as follows according to JIS. S 5002 - g6, it was necessary to inspect them visually, to test their bursting strength, tensile strength and hardness; according to IS 375 - 1966itwas necessary to inspect them visually to test their thickness, specific gravity, hardness, abrasion resisiance and flexing resistance according to cNS UDC 6g5 - 31 it was necessary to inspect them visually, to test their thickness, tensile strength, and elongation at break, according to KS M 6522 - 74 it was necessary to inspect them visually, to test their bursting strength, elongation at break and tensile sEength.